| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 24小时吸水率 | ASTM D-5700.3% | |||
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 47 | mg/1000rev |
| 比重 | ASTM D-7921.25 | |||
| 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 13 | mg/1000rev |
| 熔体流动速率 | ASTM D-123812.5g/10min | |||
| 硬度计硬度 | ASTM D-224072 | |||
| 断裂伸长 | ASTM D-638360% | |||
| 拉伸力(5%伸长) | ASTM D-63814MPa | |||
| 拉伸力(10%伸长) | ASTM D-63820MPa | |||
| 断裂拉伸力 | ASTM D-63845.8MPa | |||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 210 | J/m |
| 揉曲模量 | 23℃ | ASTM D-790 | 570 | MPa |
| 初耐撕裂性能 | ASTM D-1004200kn/m | |||
| 热畸变温度 | @0.5MPa | ASTM D-648 | 130 | ℃ |
| 维卡软化点 | ASTM D-1525207℃ | |||
| 熔点 | ASTM D-3418218℃ | |||
| 热畸变温度 | @0.18MPa | ASTM D-648 | 52 | ℃ |
| 耐揉曲切口增长性能 | ASTM D-1052>3×104 |
报价TPE 7246 美国杜邦